This 10% Zn-Al coated steel wire features a coating made of 90% zinc and 10% aluminum, which forms a dense, wear-resistant protective layer on the steel substrate. The product is manufactured on automated alloy coating production lines, with quality control procedures aligned with international standards. It is designed for industrial clients and commercial procurement projects that require long-term anti-corrosion performance in demanding working conditions. The increased aluminum content differentiates this product from lower-alloy alternatives, with measurable performance gains in high-corrosion environments.
Parameter | Value Range / Detail |
|---|---|
Coating composition | 90% zinc, 10% aluminum |
Base material | High-purity low-carbon steel |
Wire diameter | 0.5mm - 12mm |
Coating weight | 80g/㎡ - 250g/㎡ |
Operating temperature range | -50℃ - 100℃ |
Corrosion resistance ratio (vs. standard hot-dip galvanized steel wire) | 2 - 3 times |
Corrosion resistance ratio (vs. 5% Zn-Al alloy coated steel wire) | 1.2 - 1.5 times |
The alloy coating creates a uniform barrier that isolates the steel base from moisture, salt spray, acid rain and chemical media. In harsh corrosive conditions, test data shows its service life reaches 2 - 3 times that of standard hot-dip galvanized steel wire, and 1.2 - 1.5 times that of 5% Zn-Al alloy coated steel wire. This level of corrosion resistance makes the wire suitable for environments with sustained exposure to salt air and corrosive substances, reducing the frequency of replacement and maintenance for long-term projects.
The wire uses high-purity low-carbon steel as the base material, processed through precision drawing and heat treatment procedures. It exhibits defined tensile strength, toughness and fatigue resistance, and maintains dimensional stability under sustained load. The coating bonds firmly to the substrate, with a smooth surface free of zinc nodules and burrs, and resists peeling during transportation and installation. The wire can be cut, bent, twisted and woven for further processing, supporting production of wire mesh, steel strands, binding wire and fence components for different industrial uses.
The product maintains stable performance across a temperature range of -50℃ - 100℃, and works reliably under high humidity and high salinity conditions. Its weathering properties support long-term outdoor deployment without rapid performance degradation, and adapt to seasonal temperature fluctuations in coastal and inland industrial areas.
This wire supports a range of marine and offshore industrial applications, including marine aquaculture cage construction, wharf mooring system components, ship guardrail manufacturing, offshore platform fastening ties, and port facility fencing. It meets the durability requirements for long-term immersion and splash zone exposure in commercial marine operations.
For onshore coastal applications, the wire is used for chemical facility perimeter fencing, coastal construction reinforcement, cable armoring, and rockfall protection mesh in high-corrosion zones. It also supports industrial applications in high-humidity, acid-alkali exposed factory environments, reducing replacement cycles for long-term infrastructure.
For commercial procurement orders, customization is supported for specific wire diameters, coating weights, coil weights, and packaging formats. Tensile strength ranges can be adjusted to match specific project requirements, with custom tolerance controls available for precision processing applications.
Each production batch undergoes coating weight testing, adhesion testing, diameter tolerance measurement, and salt spray sample testing before delivery. Third-party inspection reports and material test certificates are available upon request for enterprise customers, with full traceability for raw material and production process records.
The 10% Zn-Al wire has doubled aluminum content in the coating compared with the 5% version. This adjustment increases corrosion resistance and wear resistance by 1.2 - 1.5 times in harsh environments, and expands the operating temperature range. It is selected for projects with more severe corrosive conditions and longer service life requirements.
Yes. Standard wire diameter covers 0.5mm - 12mm, and coating weight ranges from 80g/㎡ to 250g/㎡. Both parameters can be adjusted within the specified range according to project requirements. Custom length packaging is also available upon request to fit different construction and production schedules.
The product follows international anti-corrosion steel wire standards for coating performance and mechanical properties. Its production materials and processes meet international environmental protection requirements, making it compatible with procurement compliance rules in major global regions.